Examination of the Effect of Chemical Composition on Laser Polished Cast Irons with Spheroidal Graphite
DOI:
https://doi.org/10.24425/afe.2025.153785Abstract
Spherical Graphite Cast Iron (SGI) alloys have been used as a material in mold making for deep-drawing dies and glass molds due to their excellent machinability and thermal conductivity. Moreover, other advantages of SGI alloys are their supreme castability, to cast complex geometries in comparison to steel, and the use of up to 90 % recycled materials, especially steel scrap. This leads to a significant reduction of material and energy usage, thereby contributing to both financial savings and ecological benefits. Nevertheless, the mold application of SGI alloys is restricted by inherent limitations, including low hardness values and high surface roughness after machining and even after manual polishing. To overcome these drawbacks a laser polishing process can be beneficial to obtain a graphite-free and steel-like hard surface and to enable a very low surface roughness, optionally in combination with a final manual polishing step. According to the state of the art, the graphite in the SGI structure could not yet be entirely removed from the surface layer by laser polishing, which on one hand leads to a higher roughness and on the other hand raises the risk of cracks. In the current investigations, the SGI alloys with different chemical compositions were cast in three different geometries, machined and subsequently laser polished. After laser polishing, remelting depth and the tendency for surface cracks were investigated. In addition, the influence of graphite morphology on the laser polishing process was examined for these three alloys and three different geometries (wall thicknesses), which all have influences on the microstructure formation. This led to laser polishing parameters to produce a graphite-free, steel-like surface on SGI.References
[1] Prucha, T.E., Twarog, D., Monroe, R.W. (2008). History and trends of metal casting. ASM Handbook. https://doi.org/10.31399/asm.hb.v15.a0005186.
[2] Lopez, V., Bello, J.M., Ruiz, J. & Fernandez, B.J. (1994). Surface laser treatment of ductile irons. Journal of Materials
Science. 29, 4216-4224 DOI:10.1007/bf00414201. https://doi.org/10.1007/BF00414201.
[3] Guo, X., Stefanescu, D.M., Chuzhoy, L., Pershing, M. A. & Biltgen, G.L. (1998). A mechanical properties model for ductile iron. AFS Transactions. 105, 47-54.
[4] Labrecque, C. & Gagné, M. (1998). Review ductile iron: fifty years of continuous development. Canadian Metallurgical Quarterly. 37(5), 343-378. https://doi.org/10.1179/cmq.1998.37.5.343.
[5] Alhussein, A., Risbet, M, Bastien, A., Chobaut, J.P., Balloy, D. & Favergeon, J. (2014). Influence of silicon and addition elements on the mechanical behavior of ferritic ductile cast iron. Materials Science and Engineering: A. 605, 222-228. DOI: 10.1016/j.msea.2014.03.057.
[6] Hatate, M., Shiota, T., Takahashi, N. & Shimizu, K., (2001). Influences of graphite shapes on wear characteristics of austempered cast iron. Wear. 251, (1-12), 885-889. https://doi.org/10.1016/S0043-1648(01)00746-3.
[7] Temmler, A., Willenborg, E., & Wissenbach, K. (2012). Laser polishing. In Laser Applications in Microelectronic and Optoelectronic Manufacturing (LAMOM) XVII, February 2012 (Vol. 8243, pp. 171-183). SPIE.
[8] Temmler, A., Cortina, M., Ross, I., Küpper, M.E. & Rittinghaus, S.K., (2022). Evolution of surface topography and microstructure in laser polishing of cold work steel 1.2379 (AISI D2) using quadratic, top-hat shaped intensity distributions. Materials. 15(3), 769, 1-27. https://doi.org/10.3390/ma15030769.
[9] Fernández-Vicente, A., Pellizzari, M. & Arias, J.L. (2012). Feasibility of laser surface treatment of pearlitic and bainitic ductile irons for hot rolls. Journal of Materials Processing Technology. 212(5), 989-1002. https://doi.org/10.1016/j.jmatprotec.2011.11.013.
[10] Catalán N., Ramos-Moore, E., Boccardo, A. & Celentano, D. (2022). Surface laser treatment of cast irons: a review. Metals. 12(4), 562, 1-28. https://doi.org/10.3390/met12040562.
[11] Grum, J. & Šturm, R. (1996). Microstructure analysis of nodular iron 400-12 after laser surface melt hardening. Materials Characterization. 37(2-3), 81-88. https://doi.org/10.1016/S1044-5803(96)00063-0.
[12] Kiedrowski, T., & Wissenbach, K. (2004). Laser beam polishing of cast iron. Fraunhofer ILT Annual Report, 78.
[13] Ukar, E., Lamikiz, A., Liébana, F., Martinez, S., Tabernero, I. (2015). An industrial approach of laser polishing with differentlaser sources. Materials Science & Engineering Technology. 46, 661-667. https://doi.org/10.1002/mawe.201500324.
[14] Ukar, E., Lamikiz, A., Martinez, S. & Tabernero, I. (2014). Polishing of ductile cast iron with scan-head guided fiber laser. Materials Science Forum. 797, 151-156. https://doi.org/10.4028/www.scientific.net/MSF.797.151.
[15] Ukar, E., Lamikiz, A., Martínez, S., Estalayo, F. & Tabernero, I. (2013). Laser polishing of GGG70L cast iron with 2D scan-head. Procedia Engineering. 63, 53-59. https://doi.org/10.1016/j.proeng.2013.08.199.
[16] DIN EN 1563:2019-04; Founding — Spheroidal Graphite Cast Irons. Deutsches Institut fur Normung: Berlin, Germany, 2019.
[17] Benyounis, K.Y., Fakron, O., Abboud, J.H., Olabi, A.G. & Hashmi, M. (2005). Surface melting of nodular cast iron by Nd-YAG laser and TIG. Journal of Materials Processing Technology. 170(1-2), 127-132. https://doi.org/10.1016/j.jmatprotec.2005.04.108.
[18] Pagano, N., Angelini, V., Ceschini, L. & Campana, G. (2016). Laser remelting for enhancing tribological performances of a ductile iron. Procedia CIRP. 41, 987-991. DOI:10.1016/j.procir.2015.12.131.
[19] Nusser, C., Kumstel, J., Kiedrowski, T., Andrei Diatlov A. & Willenborg, E. (2015). Process- and material-induced surface structures during laser polishing. Advanced Engineering Materials. 17(3), 268-277. https://doi.org/10.1002/adem.201400426.
[20] Poprawe, R. (2011). Tailored light 2-laser application technology. Berlin, Germany: Springer.
[21] Krishnan, A. & Fang, F. (2019). Review on mechanism and process of surface polishing using lasers. Frontiers of Mechanical Engineering. 14(3), 299-319. https://doi.org/10.1007/s11465-019-0535-0.
[22] Temmler, A., Willenborg E. & Wissenbach, K. (2015). Design surfaces by laser remelting. Material Science & Engineering Technology. 12(A), 419-430. https://doi.org/10.1016/j.phpro.2011.03.053.
[23] Kreinest, L., Schussler, J., Özaydin, O., Kochuthundil Subhash, S., Willenborg, E. & Buhrig-Polaczek, A. (2024). Laser remelting of ductile cast iron to achieve a graphite-free surface layer for enabling a manual high-gloss finish. Metals. 14(3), 347, 1-14. https://doi.org/10.3390/met14030347.