Assessment of Thermal Conditions by Slow Solidification in Al Alloys and the Facility
DOI:
https://doi.org/10.24425/afe.2025.153788Abstract
Mold filling and casting solidification are determined by gravity driven natural convection. Also forced convection induced by rotating magnetic field influences castings microstructure. The investigations of flow effect on the aluminum casting alloys and silicon rich alloys were mainly conducted on simple cylindrical specimens and focused on the microstructure, composition and strength of electromagnetic field. Unfortunately, the temperature field in the specimens and facility were mainly omitted or not enough discussed. In the current study thermal conditions in a special facility for flow effect investigation were studied, in experimental and numerical manner, concerning Al-Si-Mg alloys with various compositions and different solid fraction curves. Solidification simulation has proven slow cooling and uniform temperature on the cross-section of the specimen and crucible, nearly uniform solidification time throughout the whole specimen, wide mushy zone and proper construction of the facility protecting electric coils. Temperature gradient and cooling rate, for alloys where almost all solid fraction and latent heat released close to solidus, were significantly higher at the solidus temperature than by liquidus, whilst in alloys where latent heat released evenly and closer to liquidus, were smoothly changing across sample and from liquidus to solidus temperature. Numerically simulated microstructure parameters like e.g. SDAS, grain size and fraction of primary phase in α-Al first alloy presented values similar and smoothly changing across specimen. It was proposed to calculate secondary dendrite arm spacing SDAS based on the specified time period, that could be responsible for melting some arms or creating new arms by dendrites, and next careful SDAS measurement across specimen was recommended. Tested facility and experimental procedure, developed for studying flow effect on the Al alloys microstructure, was proven to be very resistant to interference.References
[1] Shwe, W.H.A., Kay, T.L. & Waing, K.K.O. (2008). The effect of ageing treatment of aluminum alloys for fuselage structure-light aircraft. World Academy of Science, Engineering and Technology. International Journal of Materials and Metallurgical Engineering. 2(10), 46, 696-699.
[2] Miller, W.S., Zhuang, L., Bottema, J., Wittebrood, A.J. & de Smet, P. (2000). Recent development in aluminum alloys for the automotive industry. Materials Science and Engineering. A 280, 37-49. https://doi.org/10.1016/S0921-5093(99)00653-X.
[3] The Aluminum Association, Inc. (1998). Aluminum alloy selection and applications. A monograph of Aluminum Association Incorporation, Washington, D C.
[4] Cubberly, W.H. (1979). Properties and selection: non-ferrous alloys and pure metals. Metals Handbook (Metals Park, OH: American Society for Metals).
[5] Smith, W.F. (1993). Alluminum alloys. In B.J. Clark and Jack Maisel (Eds.), Structure and properties of engineering alloys (pp. 176-242). United States of America: McGraw-Hill Series.
[6] Mondolfo, L.F. (1976). Aluminium Alloys: Structure and Properties. London, UK: Butter worths & Co.
[7] Sarafoglou, P., I., Aristeidakis, J.S., Tzini, M-I. T. & Haidemenopoulos, G.N. (2016). Metallographic Index‐Based quantification of the homogenization state in extrudable aluminum alloys. Metals. 6(5), 121. doi: 10.3390/met6050121.
[8] Stefanescu, D. (1988). The New Metals Hand Book: Casting, ASM International.
[9] Eskin, D.G. & Katgerman, L. (2009). Solidification phenomena related to direct chill casting of aluminium alloys: fundamental studies and future challenges. Materials Technology: Advanced Performance Materials. 24(3), 152-156. DOI: 10.1179/106678509X12489478523537.
[10] Zhang, H., Nagaumi H. & Cui, J.Z. (2012). Effects of low frequency electromagnetic field of multi-physical fields during DC casting of 7xxx aluminum alloys. Advanced Science Letters. 13(1), 306-311(6). https://doi.org/10.1166/asl.2012.3762.
[11] Bojarevičs, A., Kaldre, I., Milgrāvis, M., Beinerts, T. (2017). Direct chill casting of aluminium alloys under electromagnetic. interaction. In VIII International Scientific Colloquium "Modelling for Materials Processing", 21-22 September 2017 (pp. 259-262). Riga. DOI: 10.22364/mmp2017.42.
[12] Zaïdat, K., Mangelinck-Noël, N., Moreau, R. (2007). Control of melt convection by a travelling magnetic field during the directional solidification of Al–Ni alloys. Comptes Rendus Mecanique. 335, 330-335. DOI: 10.1016/j.crme.2007.05.010.
[13] Patarić, A., Mihailović, M., Marković, M., Sokić, M., Radovanović, A. & Jordović, B. (2021). Microstructure as an essential aspect of EN AW 7075 aluminum alloy quality influenced by electromagnetic field during continuous casting process. Hemijska industrija. 75(1), 31-37. https://doi.org/10.2298/HEMIND201214006P.
[14] Kaldre, I., Milgravis, M., Bojarevics, A. & Beinerts, T. (2021). Electromagnetic processing during directional solidification of particle-strengthened aluminum alloys for additive manufacturing. Materials Proceedings. 3(1), 19, 1-4. https://doi.org/10.3390/IEC2M-09255.
[15] Patarić, A., Mihailovic, M. & Gulisija, Z. (2012). Quantitative metallographic assessment of the electromagnetic casting influence on the microstructure of 7075 Al alloy. Journal of Materials Science. 47, 793-796. DOI 10.1007/s10853-011-5855-3.
[16] Wang, X.J., Zhao, Z.H., Zuo, Y.B., Zhu, Q.F., Qu, F. & Cui, J.Z. (2009). Effects of low frequency electromagnetic field on solidification of 7050 aluminium alloy during hot top casting. Materials Science and Technology. 25(10), 1207-1210. https://doi.org/10.1179/174328408X382172.
[17] Sree Manu, K. M., Barekar, N. S., Lazaro-Nebreda J., Patel, J. B. & Fan, Z. (2021). In-situ microstructural control of A6082 alloy to modify second phase particles by melt conditioned direct chill (MC-DC) casting process – A novel approach. Journal of Materials Processing Technology. 295, 117170, 1-14. https://doi.org/10.1016/j.jmatprotec.2021.117170.
[18] Zhang, Y., Patel, J. B., Lazaro-Nebreda, J. & Fan, Z. (2018). Improved defect control and mechanical property variation in high-pressure die casting of A380 alloy by high shear melt conditioning. The Journal of The Minerals, Metals & Materials Society. 70, 2726-2730. https://doi.org/10.1007/s11837-018-3005-y.
[19] Brollo, G. L., Proni, C. T. W. & Zoqui, E. J. (2018). Thixoforming of an Fe-Rich Al-Si-Cu Alloy – thermodynamic characterization, microstructural evolution, and rheological behavior. Metals. 8(5), 332, 1-24. https://doi.org/10.3390/met8050332.
[20] Haga, T. & Suziki, S. (2001). Casting of aluminum alloy ingots for thixoforming using a cooling slope. Journal of materials processing technology. 118(1-3), 169-172. https://doi.org/10.1016/S0924-0136(01)00888-3.
[21] Eslami, M., Payandeh, M., Deflorian, F., Jarfors, A.E.W. & Zanella, C. (2018). Effect of segregation and surface condition on corrosion of rheo-HPDC Al–Si alloys. Metals. 8(4), 209, 1-18. https://doi.org/10.3390/met8040209.
[22] Mohammed, M. N., Omar, M. Z., Al-Zubaidi,S., Alhawari, K. S. & Abdelgnei, M. A. (2018). Microstructure and mechanical prperties of thixowelded AISID2 tool steel. Metals. 8(5), 316, 1-16. https://doi.org/10.3390/met8050316.
[23] Wang, H., Davidson, C. J.& St. John, D. H. (2004).Semisolid microstructural evolution of AlSi7Mg during partial remelting. Materials Science and Engineering:A.368(1-2),159-167. https://doi.org/10.1016/j.msea.2003.10.305.
[24] Mikolajczak, P.& Ratke, L. (2013). Effect of stirring in duced by rotating magnetic field on β-Al5FeSi intermetallic phases during directional solidification in AlSi alloys. International Journal of Cast Metals Research.26(6), 339-353.https://doi.org/10.1179/1743133613Y.0000000069.
[25] Mikolajczak, P.& Ratke, L. (2011). Intermetallic phases and microstructure in AlSi alloys influenced by fluid flow. The Minerals, Metals &MaterialsSociety(TMS). 10, 9781118062173.https://doi.org/10.1002/9781118062173.ch104.
[26] Mikolajczak, P. (2017). Microstructural evolution in AlMgSi alloys during solidification under electromagnetic stirring. Metals.7(3), 89, 1-16. https://doi.org/10.3390/met7030089.
[27] Mikolajczak, P. (2021). Effect of rotating magnetic field on microstructure in AlCuSi alloys. Metals. 11(11), 1804, 1-24. https://doi.org/10.3390/met11111804.
[28] Mikolajczak, P. (2023). Distribution and morphology of α-Al, Si and Fe-Richphasesin Al–Si–Fe alloys under an electromagnetic field.Materials.16(9), 3304.https://doi.org/10.3390/ma16093304.
[29] Mikolajczak, P. (2023). Morphology and distribution ofα-Al and Mn-rich phases in Al-Si-Mn alloys under an electromagnetic stirring. Archives of Foundry Engineering. 23(3), 74-87.DOI:10.24425/afe.2023.146665.
[30] Mikolajczak, P. (2023). Flow effect on Si crystals and Mn-phases in hypereutectic and eutectic Al-Si-Mn alloys. Archives of Foundry Engineering. 23(4), 72-86.DOI:10.24425/afe.2023.146681.
[31] Jie, J.C., Zou, Q.C., Wang, H.W., Sun, J.L., Lu,Y.P., Wang, T. M. &Li, T. J. (2014). Separation and purification of Si from solidification of hypereutectic Al-Si melt under rotating magnetic field. Journal of Crystal Growth. 399, 43-48. ttp://dx.doi.org/10.1016/j.jcrysgro.2014.04.003.
[32] Wenzhou, Y., Wenhui, M., Guoqiang, L., Haiyang, X., Li, S. & Dai,Y. (2014). Effect of electromagnetic stirring on the enrichment of primary silicon from Al-Si melt. Journal of Crystal Growth. 405, 23-28. http://dx.doi.org/10.1016/j.jcrysgro.2014.07.035.
[33] Ma, X., Lei, Y., Yoshikawa, T., Zhao, B.& Morita, K. (2015). Effect of solidification conditions on the silicon growth and refining using Si-Sn melt. Journal of Crystal Growth. 430,98-102. http://dx.doi.org/10.1016/j.jcrysgro.2015.08.001.
[34] Zhu, K., Hu, J., Ma, W., Wei, K., Lv, T. & Dai, Y.(2019). Effect of solidification parameters and magnetic field on separation of primary silicon from hypereutectic Ti-85 wt.% Si melt. Journal of Crystal Growth. 522, 78-85. https://doi.org/10.1016/j.jcrysgro.2019.05.012.
[35] Lv, G., Bao, Y., Zhang, Y., He, Y., Ma, W.& Leu, Y. (2018). Effects of electromagnetic directional solidification conditions on the separation of primary silicon from Al-Si alloy with high Si content. Materials Science in Semiconductor Processing.81, 139-148. https://doi.org/10.1016/j.mssp.2018.03.006.
[36] Yoshikawa, T. & Morita, K. (2005). Refining of Si by the solidification of Si-Al melt with electromagnetic force. ISIJ International. 45(7), 967-971.https://doi.org/10.2355/isijinternational.45.967.
[37] Huang, F., Zhao, L., Liu, L., Hu, Z., Chen, R. & Dong, Z. (2019). Separation and purification of Si from Sn-30Si alloy by electromagnetic semi-continuous directional solidification. Materials Science in Semiconductor Processing. 99, 54-61.https://doi.org/10.1016/j.mssp.2019.04.015.
[38] He, Y., Yang, X., Duan, L., Li, S., Chen, Z., Ma, W., Lv, G.& Xing, A. (2021). Silicon separation and purification process from hypereutectic aluminum-silicon for organosilicon use. Materials Science in Semiconductor Processing. 121, 105333, 1-11, 1-11. https://doi.org/10.1016/j.mssp.2020.105333.
[39] Jiang, W., Yu, W., Li, J., You, Z., Li, C.& Lv, X. (2018). Segregation and morphological evolution of Si phases during electromagnetic directional solidification of hypereutectic Al-Si alloys. Materials. 12(1), 10, 1-14. DOI:10.3390/ma12010010.
[40] Xue, H., Lv, G., Ma, W., Chen, D. & Yu, J. (2015). Separation mechanism of primary silicon from hypereutectic Al-Si melts under alternating electromagnetic fields. Metallurgical and Materials Transactions A. 46, 2922-2932. DOI:10.1007/s11661-015-2889-1.
[41] Sun, Jl., Zou, Qc., Jie, Jc. &Li,T. (2016). Separation of primary Si and impurity boron removal fromAl-30%Si-10% Sn melt under a traveling magnetic field. China Foundry.13(4), 284-288.https://doi.org/10.1007/s41230-016-6036-4.
[42] Zou, Q., Tian, H., Zhang, Z., Sun, C., Jie, J., Han, N. & An, X. (2020). Controlling segregation behaviour of primary Si in hypereutectic Al-Si alloy by electromagnetic stirring. Metals. 10(9), 1129, 1-13. https://doi.org/10.3390/met10091129.
[43] Zou, Q., Han, N., Zhang, Z., Jie, J., Xu, F.& An, X. (2020). Enhancing segregation behaviour of impurity by electromagnetic stirring in the solidification process ofAl-30Si alloy. Metals. 10(1), 155, 1-11. https://doi.org/10.3390/met10010155.
[44] Ren, Z. & Junze, J. (1992). Formation of a separated eutectic in Al-Si eutectic alloy. Journal of Materials Science.27, 4663-4666. https://doi.org/10.1007/BF01166003.
[45] Mikolajczak, P., Janiszewski, J., & Jackowski, J. (2019).Construction of the facility for aluminium alloys electromagnetic stirring during casting. In Advances in Manufacturing II: Volume 4-Mechanical Engineering(pp.164-175). Switzerland: Springer International Publishing.https://doi.org/10.1007/978-3-030-16943-5_15.
[46] Thermo-Calc 4.1 — Software (2024) Package from Thermo-Calc Software AB. Retrieved June 10,2023, fromwww.thermocalc.se.
[47] MAGMA (2024). Gießereitechnologie GmbH. Kackertstr.16-18. Retrieved June 5, 2024, from www.magmasoft.de.
[48] Gustafsson, G., Thorvaldsson, T. & Dunlop, G.L. (1986).The influence of Fe and Cr on the microstructure of cast. Al-Si-Mg alloys. Metallurgical Transactions A.17, 45-52. https://doi.org/10.1007/BF02644441.
[49] Prakash S.P., Om P. & Devendra K. (2020). Structure and mechanical behavior of in situ developed Mg 2Si phase in magnesium and aluminum alloys – a review. RSC Advances. 10(61), 37327-37345. http://dx.doi.org/10.1039/ D0RA02744H.
[50] Yan, F. (2013). Development of high strength Al-Mg2Si-Mg based alloy for high pressure die casting process. PhD thesis. BCAST. Brunel University Uxbridge, UB8 3PH United Kingdom.
[51] Hunt, J.D. (2001). Pattern formation in solidification. Science and Technology of Advanced Materials. 2(1), 147-155. https://doi.org/10.1016/S1468-6996(01)00040-7.
[52] Hunt, J.D. & Lu, S.Z. (1996) Numerical modeling of cellular/dendritic array growth: Spacing and structure predictions. Metallurgical and Materials Transactions A. 27, 611-623. https://doi.org/10.1007/BF02648950.
[53] Stefanescu, D. (2009). Science and engineering of casting solidification. Boston, MA, USA: Springer. https://doi.org/10.1007/b135947.
[54] Kattamis, T.Z. & Flemings, M.C. (1965). Dendrite morphology. Microsegregation and Homogenization of low alloy steel. Transactions of the Metallurgical Society of AIME. 233(5), 992-999.
[55] Rappaz, M. & Boettinger, W. (1999). On dendritic solidification of multicomponent alloys with unequal liquid diffusion coefficients. Acta Materialia. 47(11), 3205-3219. https://doi.org/10.1016/S1359-6454(99)00188-3.
[56] Bouchard, D. & Kirkaldy, J.S. (1997). Prediction of dendrite arm spacing in unsteady- and steady-state heat flow. Metallurgical and Materials Transactions B. 28(4), 651-663. https://doi.org/10.1007/s11663-997-0039-x.
[57] Steinbach, S. & Ratke, L. (2007). The influence of fluid flow on the microstructure of directionally solidified AlSi-base alloys. Metallurgical and Materials Transactions A. 38, 1388-1394. https://doi.org/10.1007/s11661-007-9162-1.
[58] Mortensen, A. (1991). On the rate of dendrite arm coarsening. Metallurgical Transactions A. 1991, 22, 569-574. https://doi.org/10.1007/BF02656824.
[59] Voorhees, P.W. & Glicksman, M.E. (1984). Ostwald ripening during liquid phase sintering — Effect of volume fraction on coarsening kinetics. Metallurgical and Materials Transactions A. 15, 1081-1088. https://doi.org/10.1007/BF02644701.
[60] Ferreira, A.F., Castro, J.A. & Ferreira, L.O. (2017). Predicting secondary-dendrite arm spacing of the Al-4.5wt%Cu alloy during unidirectional solidification. Materials Research. 20(1), 68-75. https://doi.org/10.1590/1980-5373-MR-2015-0150.