Cooling Rate and Gradient by Fe- and Mn-Rich Phases Precipitation in AlCuSi Alloys
DOI:
https://doi.org/10.24425/afe.2026.158030Abstract
Gravity influences mold filling and solidification. In foundry engineering, apart from well-known gravity, centrifugal and pressure casting, technologies for casting by forced convection are being developed, where the application of a magnetic field plays a key role. Till now, the efficacy of forced flow in numerous studies have been conducted, including silicon extraction and aluminum alloys. The weakness of these studies is the fact, that they were conducted on small samples, mainly cylindrical shaped, where the cooling rate, gradient and temperature field were poorly investigated and discussed. In the present study, , thermal conditions like temperature gradient G and cooling rate R by the growth of occurring phases were studied using numerical simulation, concerning the facility applied in the investigations on the effect of rotating magnetic field. In cylindrical samples from base AlCuSi alloys, cooling rate R and temperature gradient G presented dependence from: calculation method for R and G (specified temperature or solid fraction in the TL-TS range), the place of measurement in the sample and from solid fraction curve determined by the alloy composition. β-Al9Fe2Si2 phases precipitated at G=0.050-0.103 ˚C/mm and R=0.103-0.135 ˚C/s near to liquidus temperature and at G=0.043-0.387 ˚C/mm and R=0.318-0.404 ˚C/s near to solidus in AlCu4Si6Fe1 alloy, whilst at G=0.021-0.225 ˚C/mm and R=0.467-0.475 ˚C/s near to liquidus and at G=0.165-0.284 ˚C/mm and R=0.151-0.862 ˚C/s near to solidus in AlCu10Si10Fe1 alloy. Al15Si2Mn4 phases precipitated at G=0.008-0.281 ˚C/mm and R=0.539-0.552 ˚C/s near to liquidus, whilst at G=0.050-0.322 ˚C/mm and R=0.292-0.356 ˚C/s near to solidus in the AlCu4Si6Mn2 alloy. In the prediction of secondary dendrite arm spacing and AlSi eutectic spacing new approach was tested and appropriate values of materials coefficient’s have been established. Negligible impact of errors in processing parameters set by experimental procedure was observed.
References
[1] Shwe, W.H.A., Kay, T.L. & Waing, K.K.O. (2008). The effect of ageing treatment of aluminum alloys for fuselage structure-light aircraft. International Journal of Materials and Metallurgical Engineering. 2(10), 245-248.
[2] Miller, W.S., Zhuang, L., Bottema, J., Wittebrood, A.J.,
de Smet, P., Haszler A. & Vieregge A. (2000). Recent development in aluminum alloys for the automotive industry. Journal of Materials Science and Engineering A. 280(1), 37–49. DOI: 10.1016/S0921-5093(99)00653-X.
[3] The Aluminum Association. (1998). Aluminum alloy selection and applications. Washington, D C.
[4] Cubberly, W.H. (1979). Properties and selection: non-ferrous alloys and pure metals. Metals Handbook. American Society for Metals.
[5] Smith, W.F. (1993). Structure and properties of engineering alloys. McGraw-Hill.
[6] Mondolfo, L.F. (1976). Aluminium Alloys: Structure and Properties. Butterworths & Co.: London, UK.
[7] Gao, N. (Ed.). (2018). Aluminum alloys. MDPI.
[8] Stefanescu, D. (1988). The New Metals Hand Book. ASM International.
[9] Ferreira, A.F., Castro, J.A. & Ferreira, L.O. (2017). Predicting secondary-dendrite arm spacing of the Al-4.5wt%Cu alloy during unidirectional solidification. Materials Research. 20(1), 68-75. DOI: 10.1590/1980-5373-MR-2015-0150.
[10] Barros, A.S., Magno, I.A., Souza, F.A., Mota, C.A., Moreira, A.L., Silva, M.A. & Rocha, O.L. (2015). Measurements of microhardness during transient horizontal directional solidification of Al-rich Al-Cu alloys: Effect of thermal parameters, primary dendrite arm spacing and Al2Cu intermetallic phase. Metals and Materials International. 21(3), 429-439. DOI: 10.1007/s12540-015-4499-2.
[11] Lei, Q., Wang, J. & Misra, A. (2021). Mechanical behavior of Al–Al2Cu–Si and Al–Al2Cu eutectic alloys. Crystals. 11(2), 194, 1-9. https://doi.org/10.3390/cryst11020194.
[12] Flemings, M. (1991). Behavior of metal alloys in the semisolid state. Metallurgical Transactions B. 22B, 269-293. https://doi.org/10.1007/BF02651227.
[13] Kaldre, I., Milgravis, M., Bojarevics, A. & Beinerts, T. (2021). Electromagnetic processing during directional solidification of particle-strengthened aluminum alloys for additive manufacturing. Materials Proceedings. 3(1), 19, 1-4. https://doi.org/10.3390/IEC2M-09255.
[14] Wang, X.J., Zhao, Z.H., Zuo, Y.B., Zhu, Q.F., Qu, F. & Cui, J.Z. (2009). Effects of low frequency electromagnetic field on solidification of 7050 aluminium alloy during hot top casting. Materials Science and Technology. 25(10), 1207-1210. https://doi.org/10.1179/174328408X382172.
[15] Patarić A., Mihailović M., Marković M., Sokić M., Radovanović A. & Jordović B. (2021). Microstructure as an essential aspect of EN AW 7075 aluminum alloy quality influenced by electromagnetic field during continuous casting process. Hemijska industrija. 75(1), 31-37. DOI: 10.2298/HEMIND201214006P.
[16] Patarić A., Mihailovic M. & Gulisija Z. (2012). Quantitative metallographic assessment of the electromagnetic casting influence on the microstructure of 7075 Al alloy. Journal of Materials Science. 47, 793-796. DOI: 10.1007/s10853-011-5855-3.
[17] Zaïdat K., Mangelinck-Noël N. & Moreau R. (2007). Control of melt convection by a travelling magnetic field during the directional solidification of Al–Ni alloys. Comptes Rendus Mecanique. 335, 330-335. DOI:10.1016/j.crme.2007.05.010.
[18] Sree Manu, K.M., Barekar, N.S., Lazaro-Nebreda J., Patel, J.B. & Fan, Z. (2021). In-situ microstructural control of A6082 alloy to modify second phase particles by melt conditioned direct chill (MC-DC) casting process – A novel approach. Journal of Materials Processing Technology. 295, 117170, 1-10.
https://doi.org/10.1016/j.jmatprotec.2021.117170.
[19] Zhang, Y., Patel, J.B., Lazaro-Nebreda, J. & Fan, Z. (2018). Improved defect control and mechanical property variation in high-pressure die casting of A380 alloy by high shear melt conditioning. JOM. 70, 2726-2730. https://doi.org/10.1007/s11837-018-3005-y.
[20] Wang, H., Davidson, C.J. & St. John, D.H. (2004). Semisolid microstructural evolution of AlSi7Mg during partial remelting. Materials Science & Engineering: A. 368(1-2), 159-167. https://doi.org/10.1016/j.msea.2003.10.305.
[21] Brollo, G.L., Proni, C.T.W. & Zoqui, E.J. (2018). Thixoforming of an Fe-Rich Al-Si-Cu alloy—thermodynamic characterization, microstructural evolution, and rheological behavior. Metals. 8(5), 332, 1-24. https://doi.org/10.3390/met8050332.
[22] Haga T. & Suziki, S. (2001). Casting of aluminum alloy ingots for thixoforming using a cooling slope. Journal Materials Processing Technology. 118 (1-2), 169-172. https://doi.org/10.1016/S0924-0136(01)00888-3.
[23] Eslami, M., Payandeh, M., Deflorian, F., Jarfors, A.E.W. & Zanella, C. (2018). Effect of segregation and surface condition on corrosion of Rheo-HPDC Al–Si alloys. Metals. 8(4), 209, 1-18. https://doi.org/10.3390/met8040209.
[24] Mohammed, M.N., Omar, M.Z., Al-Zubaidi, S., Alhawari, K.S. & Abdelgnei, M.A. (2018). Microstructure and mechanical properties of thixowelded AISI D2 tool steel. Metals. 8(5), 316, 1-16. https://doi.org/10.3390/met8050316.
[25] Eskin D.G. & Katgerman L. (2009). Solidification phenomena related to direct chill casting of aluminium alloys: fundamental studies and future challenges. Materials Technology: Advanced Performance Materials. 24(3), 152-156. DOI: 10.1179/106678509X12489478523537.
[26] Zhang, H., Nagaumi H. & Cui, J.Z. (2012). Effects of low frequency electromagnetic field of multi-physical fields during DC casting of 7XXX aluminum alloys. Advanced Science Letters. 13(1), 306-311. https://doi.org/10.1166/asl.2012.3762.
[27] Bojarevičs, A., Kaldre, I., Milgrāvis, M., Beinerts, T. (2017). Direct chill casting of aluminium alloys under electromagnetic interaction. In VIII International Scientific Colloquium "Modelling for Materials Processing", 21-22 September 2017 (pp. 259-262). Riga, Latvia. DOI: 10.22364/mmp2017.42.
[28] Mikolajczak, P. & Ratke, L. (2013). Effect of stirring induced by rotating magnetic field on β-Al5FeSi intermetallic phases during directional solidification in AlSi alloys. International Journal of Cast Metals Research. 26(6), 339-353. https://doi.org/10.1179/1743133613Y.0000000069.
[29] Mikolajczak, P. & Ratke, L. (2011). Intermetallic phases and microstructure in AlSi alloys influenced by fluid flow. The Minerals, Metals & Materials Society. TMS. 10, 9781118062173, 825-832. https://doi.org/10.1002/9781118062173.ch104.
[30] Mikolajczak, P. (2026). AlSiMg alloys microstructure determined by flow effect during slow solidification. Archives of Foundry Engineering. 26(1), 52-67. DOI: 10.24425/afe.2026.157969.
[31] Mikolajczak, P. (2021). Effect of rotating magnetic field on microstructure in AlCuSi alloys. Metals. 11(11), 1804, 1-23. https://doi.org/10.3390/met11111804.
[32] Mikolajczak, P. (2023). Morphology and distribution of α-Al and Mn-rich phases in Al-Si-Mn alloys under an electromagnetic stirring. Archives of Foundry Engineering. 23(3), 74-87. DOI: 10.24425/afe.2023.146665.
[33] Mikolajczak, P. (2023). Flow effect on Si crystals and Mn-phases in hypereutectic and eutectic Al-Si-Mn alloys. Archives of Foundry Engineering. 23(4), 72-86. DOI: 10.24425/afe.2023.146681.
[34] Mikolajczak, P. (2023). Distribution and morphology of α-Al, Si and Fe-rich phases in Al–Si–Fe alloys under an electromagnetic field. Materials. 16(9), 3304, 1-31. https://doi.org/10.3390/ma16093304.
[35] Mikolajczak, P. (2017). Microstructural evolution in AlMgSi alloys during solidification under electromagnetic stirring. Metals. 7(3), 89, 1-16. https://doi.org/10.3390/met7030089.
[36] Mikolajczak, P. (2025). Assessment of thermal conditions by slow solidification in Al alloys and the facility. Archives of Foundry Engineering. 25(2), 5-20. DOI: 10.24425/afe.2025.153788.
[37] Lv, G., Bao, Y., Zhang, Y., He, Y., Ma, W. & Leu, Y. (2018). Effects of electromagnetic directional solidification conditions on the separation of primary silicon from Al-Si alloy with high Si content. Materials Science in Semiconductor Processing. 81, 139-148. https://doi.org/10.1016/j.mssp.2018.03.006.
[38] He, Y., Yang, X., Duan, L., Li, S., Chen, Z., Ma, W., Lv, G. & Xing, A. (2021). Silicon separation and purification process from hypereutectic aluminum-silicon for organosilicon use. Materials Science in Semiconductor Processing. 121(1), 105333, 1-11. https://doi.org/10.1016/j.mssp.2020.105333.
[39] Wenzhou, Y., Wenhui, M., Guoqiang, L., Haiyang, X., Li, S. & Dai, Y. (2014). Effect of electromagnetic stirring on the enrichment of primary silicon from Al-Si melt. Journal of Crystal Growth. 405, 23-28. http://dx.doi.org/10.1016/j.jcrysgro.2014.07.035.
[40] Jie, J.C., Zou, Q.C., Wang, H.W., Sun, J.L., Lu, Y.P., Wang, T.M. & Li, T.J. (2014). Separation and purification of Si from solidification of hypereutectic Al-Si melt under rotating magnetic field. Journal of Crystal Growth. 399, 43-48. http://dx.doi.org/10.1016/j.jcrysgro.2014.04.003.
[41] Zhu, K., Hu, J., Ma, W., Wei, K., Lv, T. & Dai, Y. (2019). Effect of solidification parameters and magnetic field on separation of primary silicon from hypereutectic Ti-85 wt.% Si melt. Journal of Crystal Growth. 522, 78-85. https://doi.org/10.1016/j.jcrysgro.2019.05.012.
[42] Yoshikawa, T. & Morita, K. (2005). Refining of Si by the solidification of Si-Al melt with electromagnetic force. ISIJ International. 45(7), 967-971. https://doi.org/10.2355/isijinternational.45.967.
[43] Ma, X., Lei, Y., Yoshikawa, T., Zhao, B. & Morita, K. (2015). Effect of solidification conditions on the silicon growth and refining using Si-Sn melt. Journal of Crystal Growth. 430, 98-102. http://dx.doi.org/10.1016/j.jcrysgro.2015.08.001.
[44] Huang, F., Zhao, L., Liu, L., Hu, Z., Chen, R. & Dong, Z. (2019). Separation and purification of Si from Sn-30Si alloy by electromagnetic semi-continuous directional solidification. Materials Science in Semiconductor Processing. 99, 54-61. https://doi.org/10.1016/j.mssp.2019.04.015.
[45] Xue, H., Lv, G., Ma, W., Chen, D. & Yu, J. (2015). Separation mechanism of primary silicon from hypereutectic Al-Si melts under alternating electromagnetic fields. Metallurgical and Materials Transactions A. 46, 2922-2932. DOI: 10.1007/s11661-015-2889-1.
[46] Jiang, W., Yu, W., Li, J., You, Z., Li, C. & Lv, X. (2018). Segregation and morphological evolution of Si phases during electromagnetic directional solidification of hypereutectic Al-Si alloys. Materials. 12(1), 10, 1-14. DOI:10.3390/ma12010010.
[47] Sun, Jl., Zou, Qc., Jie, Jc. & Li, T. (2016). Separation of primary Si and impurity boron removal from Al-30%Si-10%Sn melt under a traveling magnetic field. China Foundry. 13(4), 284-288. https://doi.org/10.1007/s41230-016-6036-4.
[48] Zou, Q., Han, N., Zhang, Z., Jie, J., Xu, F. & An, X. (2020). Enhancing segregation behaviour of impurity by electromagnetic stirring in the solidification process of Al-30Si alloy. Metals. 10(1), 155, 1-11. DOI:10.3390/met10010155.
[49] Ren Z. & Junze J. (1992). Formation of a separated eutectic in Al-Si eutectic alloy. Journal of Materials Science. 27, 4663-4666. https://doi.org/10.1007/BF01166003.
[50] Zou, Q., Tian, H., Zhang, Z., Sun, C., Jie, J., Han, N. & An, X. (2020). Controlling segregation behaviour of primary Si in hypereutectic Al-Si alloy by electromagnetic stirring. Metals. 10(9), 1129, 1-13. https://doi.org/10.3390/met10091129.
[51] Mikolajczak, P., Janiszewski, J. & Jackowski, J. (2019). Construction of the facility for aluminium alloys electromagnetic stirring during casting. In Gapiński B., Szostak M., Ivanov V. (Eds.), Advances in manufacturing II. Vol. 4. Mechanical Engineering (pp. 164-175). Cham, Switzerland, Springer. https://doi.org/10.1007/978-3-030-16943-5_15.
[52] Magmasoft 6.0.0.6 - MAGMA Gießereitechnologie GmbH. Kackertstr. 16-18. 52072 Aachen. Germany. www.magmasoft.de.
[53] Thermo-Calc 4.1—Software package from Thermo-Calc Software AB. Stockholm. Sweden. Retrieved June 10, 2023 from www.thermocalc.se.
[54] Gustafsson, G., Thorvaldsson, T. & Dunlop, G.L. (1986). The influence of Fe and Cr on the microstructure of cast Al-Si-Mg alloys. Metallurgical and Materials Transactions A. 17, 45-52. https://doi.org/10.1007/BF02644441.
[55] Prakash, S.P., Om, P. & Devendra, K. (2020). Structure and mechanical behavior of in situ developed Mg2Si phase in magnesium and aluminum alloys – a review. The Royal Society of Chemistry. RSC Advances. 10(61), 37327-37345. http://dx.doi.org/10.1039/D0RA02744H.
[56] Yan, F. (2013). Development of high strength Al-Mg2Si-Mg based alloy for high pressure diecasting process. PhD Thesis, BCAST, Brunel University Uxbridge, UB8 3PH United Kingdom.
[57] Hunt, J.D. (2001). Pattern formation in solidification. Science and Technology of Advanced Materials. 2, 147-155. https://doi.org/10.1016/S1468-6996(01)00040-7.
[58] Hunt, J.D. & Lu, S.Z. (1996). Numerical modeling of cellular/dendritic array growth: Spacing and structure predictions. Metallurgical and Materials Transactions A. 27, 611-623. https://doi.org/10.1007/BF02648950.
[59] Stefanescu, D. (2009). Science and Engineering of Casting and Solidification. Boston, MA, USA: Springer. https://doi.org/10.1007/b135947.
[60] Kattamis, T.Z. & Flemings, M.C. (1965). Dendrite morphology. Microsegregation and homogenization of low alloy steel. Transactions of the Metallurgical Society of AIME. 233(5), 992-999.
[61] Rappaz, M. & Boettinger, W. (1999). On dendritic solidification of multicomponent alloys with unequal liquid diffusion coefficients. Acta Materialia. 47(11), 3205-3219. https://doi.org/10.1016/S1359-6454(99)00188-3.
[62] Bouchard, D. & Kirkaldy, J.S. (1997). Prediction of dendrite arm spacing in unsteady- and steady-state heat flow. Metallurgical and Materials Transactions B. 28B, 651-663. https://doi.org/10.1007/s11663-997-0039-x.
[63] Steinbach, S. & Ratke, L. (2007). The influence of fluid flow on the microstructure of directionally solidified AlSi-base alloys. Metallurgical and Materials Transactions A. 38, 1388-1394. https://doi.org/10.1007/s11661-007-9162-1.
[64] Mortensen, A. (1991). On the rate of dendrite arm coarsening. Metallurgical and Materials Transactions A. 22, 569-574. https://doi.org/10.1007/BF02656824.
[65] Voorhees, P.W. & Glicksman, M.E. (1984). Ostwald ripening during liquid phase sintering—Effect of volume fraction on coarsening kinetics. Metallurgical and Materials Transactions A. 15A, 1081–1089. https://doi.org/10.1007/BF02644701.
[66] Neumann-Heyme, H., Shevchenko, N., Lei, Z., Eckert, K., Keplinger, O., Grenzer, J., Beckermann, C. & Eckert, S. (2018). Coarsening evolution of dendritic sidearms: From synchrotron experiments to quantitative modeling. Acta Materialia. 146, 176-186, ISSN 1359-6454, https://doi.org/10.1016/j.actamat.2017.12.056.
[67] Cool, T. & Voorhees, P.W. (2017). The evolution of dendrites during coarsening: Fragmentation and morphology. Acta Materialia. 127, 359-367, https://doi.org/10.1016/j.actamat.2017.01.029.
[68] Ruvalcaba, D., Eskin, D. G., Mathiesen, R. H., Arnberg, L. & Katgerman, L. (2009). Influence of dendrite arrangement on coarsening during solidification of high-solute Al alloys. International Journal of Cast Metals Research. 22(1-4), 271-274. https://doi.org/10.1179/136404609X367957.
[69] Terzi, S., Salvo, L., Suery, M., Dahle, A.K. & Boller, E. (2010). Coarsening mechanisms in a dendritic Al–10% Cu alloy. Acta Materialia. 58(1), 20-30. https://doi.org/10.1016/j.actamat.2009.08.052.
[70] Kasperovich, G., Genau, A. & Ratke, L. (2011). Mushy zone coarsening in an AlCu30 alloy accelerated by a rotating magnetic field. Metallurgical and Materials Transactions A. 42, 1657-1666. https://doi.org/10.1007/s11661-010-0542-6.
[71] Kurz. W, Fisher D.J. Fundamentals of Solidification. Switzerland: Trans Tech Publications.
[72] Dantzig, J.A., Rappaz, M. (2009). Solidification. Lausanne, Switzerland: EPFL Press.
[73] Jackson, K.A., Hunt, J.D. (1966). Lamellar and rod eutectic growth. Transactions of the Metallurgical Society of AIME. 236, 1129-1142.
Downloads
Published
How to Cite
Issue
Section
License
Copyright (c) 2026 Archives of Foundry Engineering
This work is licensed under a Creative Commons Attribution 4.0 International License.